FLUX CORED WIRE/FRW-316L

 

FRW-316L

ACCORDING WITH GB/ T 17853 E316LT1-1/-4 CORRESPONDING WITH AWS A5.22 E316LT1-1 JIS Z3323 YF-316LC

Introduction & Characteristics:
FRW-316L is a rutile type flux cored wire for low carbon 18%Cr-12%Ni-2%Mo stainelss steel. It is used for all position welding to be used with CO₂ or Argon + CO₂ mixed shielding gases.This wire recommended for high deposition rates in the flat and horizbontal position.

Instructions:
1.The oil stains and rust on the weldments should be cleared away.
2. Designed for welding with CO₂ or Argon + CO₂ mixed shielding gases
3. When welding, the gas flow rate is generally 20～25L/min.

Chemical compostiton of deposited metal (shield gas:CO₂)

C	Mn	Si	P	S	Ni	Cr	Mo
0.027	1.51	0.40	0.026	0.003	12.75	19.61	2.28

Mechanical properties of deposited metal (shield gas:CO₂)

Yield Strength Mpa(σb)	Elongation %(δ5)	Impact Value -20℃(J)
580	45	32

Sizes available and recommended currents(DC-EP)

Diameter(mm)		0.9	1.2	1.6
Current(A)	F,HF	130-180	180-220	250-290
	V-up OH	100-140	120-160	220-270

Package

Dia(mm)	1.2	1.4	1.6
Spool(kg)/(lbs)	5,12.5,15,20/11,28,33

Welding positions